Nickel Alloy Incoloy 800HT UNS N08811

\

Short Introduction:

HY 800HT / ​​인코 로이 800HT / ​​UNS N08811 / W.Nr.1.4959 X 8 NiCrAlTi 32-21 / BS NA 15 (HT)면심 입방 격자 구조이다. 매우 낮은 탄소 centent 증가의 Ti : C 레이트 구조, 항 알러지 및 항 입계 부식의 안정성을 향상시킨다. 950 ℃의 저온 열처리는 미세 입자 구조를 확인합니다.


  • Fob price: US $ 25 - 80 / Kilogram
  • Min.order quantity: 300kg
  • Port: Shanghai
  • Payment terms: L/C,T/T,30% down payment after order, balance against copy of B/L
  • Product Detail

    Product Tags

    HY의 800HT

    재질 등급과 동등

    인코 로이 800HT / ​​UNS N08811 / W.Nr.1.4959 X 8 NiCrAlTi 32-21 / BS NA 15 (HT)

    인코 로이 800H 화학 성분 :

    Alloy

    %

    Ni

    Cr

    Fe

    C

    Mn

    Si

    Cu

    S

    Al

    Ti

    800

    Min.

    30

    19

    0.15

    0.15

    Max.

    35

    23

    balance

    0.1

    1.5

    1

    0.75

    0.015

    0.6

    0.6

    800H

    Min.

    30

    19

    0.05

    0.15

    0.15

    Max.

    35

    23

    balance

    0.1

    1.5

    1

    0.75

    0.015

    0.6

    0.6

    800HT

    Min.

    30

    19

    0.06

    0.15

    0.15

    Max.

    35

    23

    balance

    0.1

    1.5

    1

    0.75

    0.015

    0.6

    0.6

    AI + 티 : 0.85-1.20

    인코 로이 800H 물성

    Density

    8.0 g / ㎤의

    Melting point

    1,350에서 1,400 사이 ℃

    인코 로이 800H 합금 실내 온도에서 최소한의 기계적 특성

    Alloy

    Tensile strength

    Yield strength

    Elongation

    RM은 N / mm² 인

    RP 0 2 N / mm² 인

    5 %

    800

    500

    210

    35

    800H

    450

    180

    35

    아래 800H의 특징 :
    500 ℃의 매우 높은 온도의 물 매체 1. 우수한 내식성.
    내식성 스트레스 2.Good
    3.Good 가공

    HY 800HTMetallurgical 구조 :
    800H는 면심 입방 격자 구조이다. 매우 낮은 탄소 centent 증가 티 : C 비율
    상기 구조의 안정성, 항 알러지 및 항 입계 부식을 향상시킨다. 950 ℃의 저온 열처리는 미세 입자 구조를 확인합니다.

    HY 800HTCorrosion 저항 :
    800H 미디어 많은 종류의 부식이 될 수 없다. 높은 니켈 함량은 더 공식과 균열 부식 균열에 저항 할 수 만든 그것에 물 부식 condition.High 크롬 함량 양호한 응력 부식 균열 내성 특성을 만들었다. 이 합금은 질산, 유기산 부식을 견딜 수 있지만, 황산 및 염산 너무 미세하지 않다.
    800H 아니라 산화 모두 물, 연기, 스팀, 공기 및 이산화탄소의 혼합 염, 할라이드 어쩌면 작은 공식뿐만 아니라, 매우 우수한 내식성 특성을 비는 산화에 우수한 내식성.

    HY 800HTApplication 범위와 분야
    nitrc 산의 1.Nitrate 콘덴서 - 부식 방지
    2.Steam 난방 파이프 - 아주 좋은 기계적 성질
    요소 튜브 아주 좋은 기계적 성질을 3.Heat

    최대 500 ℃ enviornment, 소둔 합금 공급 상태 변화의 응용 프로그램에 대한.

     

    Specifications:

    Rod, Bar, Wire, Forgings, and Forging Stock

    ASTM B 408 & ASME SB 408;ASTM B 564 & ASME SB 564;ASME Code Case 1325;ASME Code Case 1949;ISO 9723;ISO 9724;ISO 9725;BS 3076NA15;BS 3075NA15;SEW 470;VdTÜV 412 & 434;DIN 17460;EN 10095

    Plate, Sheet, and Strip

    ASTM A 240/A 480;ASME SA 240/SA 480;ASTM B 409/B 906;ASME SB 409/SB 906;ASME Code Case 1325;ASME Code Case 2339;BS 3072NA15;BS 3073NA15;SEW 470;VdTÜV 412 & 434;DIN 17460;EN 10028-7 & EN 10095     

    Pipe & Tube

    ASTM B 163;ASME SB 163;ASTM B 407/B 829;ASME SB 407/SB 829;ASTM B 514/B 775;ASME SB 514/SB 775;ASTM B 515/B 751;ASME SB 515/SB 751;ASME Code Case 1325 and 1983;BS 3074NA15;SEW 470;VdTÜV 412 & 434;ISO 6207;DIN 17459

    Fittings

    ASTM B 366/ASME SB 366

     

    Regular shape for all kinds of alloys
    Form Specification Supply Form Others
    Sheet Thickness:0.40-4.75mm,General Width:1000、1219、1500mm Whole Coil or piece of it Cold Annealed,Surface 2B、2E
    Plate Thickness:4.76-60mm,Width:1500、2000、2500mm,Length:3000、6000、8000、8500mm(Under 10mm plate can be coiled) Whole Coil or piece of it Single hot rolling,Solid solution annealed state,Surface 1D
    Belt Thickness:0.10-3.0mm,Width:50-500mm Whole Coil or Specified size Cold Annealed,Surface 2B、2E
    Bar & Rod Rolled barΦ5-45mm,Length≤1500mm Polished Bar(circle、Square) Solution annealing,descaling
    Forged barΦ26-245mm,Length≤4000mm
    Weld tube Outer diameterΦ4.76-135mm,Wall Thickness0.25-4.00mm,Length:≤35000 mm Base on your requirement
    Seamless Tube Outer diameterΦ3-114mm,Wall Thickness0.2-4.5mm Base on your requirement
    Wire Outer diameterΦ0.1-13mm Base on your requirement Ni & Ni alloy, Ti & Ti alloy
    Forged piece discs,rings,squares,blocks,slabs Base on your requirement Steel, Alloy
    Flangs All kinds of Flangs Base on your requirement Steel, Alloy
    Welding Material Coil wire Φ0.025mm-1.6mm Base on your requirement Certificate of Origin:America, Sweden, Britain, Germany, Austria, Italy, France.
    Straight WireΦ1.6mm-4.0mm
    Welding rodΦ1.2mm-4.0mm
    Tube Elbow, three links, four links, different diameter size Base on your requirement Ni & Ni alloy, Ti & Ti alloy
    Explosive bonded laminate Raw Sheet Thickness≥2mm Base on your requirement Ni & Ni alloy, Ti & Ti alloy